Immobilizing chromium in stainless steel slags with MnO addition

This work investigates the stabilizing impact of MnO on the leaching behavior of hazardous Cr-containing CaO-SiO₂-Al₂O₃-Cr₂O₃-MnO stainless steel slags after equilibrating at various elevated temperatures and evaluates the potential immobilization of Cr into a MnCr₂O₄ spinel phase from the existing Cr₂O₃ phase. The MnCr₂O₄ spinel phase was found to be an excellent Cr-stabilizer in stainless steel slags, where the leaching tendency of potentially hazardous Cr-related ions decreased with higher MnO content and lower equilibration temperatures within the range of 0 to 15 mass pct. and 1500 to 1300°C, respectively. Thermodynamic calculations by conducting the phase stability diagram also showed that the MnCr₂O₄ spinel phase was relatively stable and the Ca₃Si₂O₇ (Ca_3-xMn_xSi₂O₇) phase was relatively unstable compared with other crystal phases in acid extractant with pH value of 3.2. Combined with the scanning electron microscopy and X-ray powder diffraction results along with the thermodynamic calculations, the leached Cr-related ions was predominantly originating from the unstable amorphous glass phase.