Molten-Salt Synthesis of Ba1–xPbxTiO3 in the System BaTiO3–PbCl2

Ba_{1– x} Pb _x TiO₃ powder with a fixed composition was prepared by the reaction of BaTiO₃ powders with molten PbCl₂at various PbCl₂/BaTiO₃ molar ratios at 600° and 800°C in a nitrogen atmosphere. When 0.1 μm powder was used, the reaction was finished when x = 0.9. Two phases of BaTiO₃and a solid solution of Ba_{1– x} Pb _x TiO₃ coexisted, but the final phase gave a solid solution of Ba_{1– x} Pb _x TiO₃ at 800°C. When 0.5 μm powder was used, the two phases coexisted in the products at 600°C at PbCl₂/BaTiO₃= 1.0. A sintered compact of Ba_{1– x} Pb _x TiO₃ powders solid solution was prepared by hot isostatic pressing, and its dielectric constant was measured in the temperature range 20°–550°C.