Near infrared light-induced photocurrent in NaYF4:Yb3+, Er3+/WO2.72 composite film

Spectral conversion technology based on NaYF₄:Yb³⁺, Er³⁺ upconversion nanoparticles was extensively used to improve photovoltaic conversion efficiency of solar cells. However, the response mismatch between absorption of semiconductors and upconversion luminescence (UCL) limits the application of spectral conversion technology. Nonstoichiometric WO_2.72 nanoparticles display the broad absorption from visible to near-infrared region due to the presence of oxygen vacancy, which is overlapped with the UCL of NaYF₄:Yb³⁺, Er³⁺ nanoparticles. Thus, the combination between NaYF₄:Yb³⁺, Er³⁺ nanoparticles, and nonstoichiometric WO_2.72 provides a possibility for designing a novel UCL spectral converted solar cells. In this work, composite film consisted of NaYF₄:Yb³⁺, Er³⁺ nanoparticles, and WO_2.72 nanofibers was prepared. The UCL of NaYF₄:Yb³⁺, Er³⁺/WO_2.72 film was decreased in contrast to pure NaYF₄:Yb³⁺, Er³⁺ nanoparticles due to energy transfer from NaYF₄:Yb³⁺, Er³⁺ nanoparticles to WO_2.72 nanofibers. The NaYF₄:Yb³⁺, E³⁺/WO_2.72film exhibits the photocurrent generation upon the 980 nm excitation. This novel UCL spectral converted solar cells based on the broad absorption of defects in the WO_2.72 host will provide a novel view for photovoltaic devices.