Double pyrovanadates CaMgV2O7: Formation mechanism,phase structure,and thermodynamic properties

A double pyrovanadate CaMgV₂O₇ sample was synthesized via a facile solid-state route under an air atmosphere. The nonequilibrium formation pathways of the CaMgV₂O₇ were investigated via powder X-ray diffraction. A multistep reactions path (metavanadates–pyrovanadates–double pyrovanadate CaMgV₂O₇) was proposed to describe the formation of the CaMgV₂O₇ considering the thermodynamic and kinetic factors. The cell unit parameters of the CaMgV₂O₇ sample indicated the crystallization according to a monoclinic system with space group P12/c1(14), and the lattice parameters of a = 6.756 Å, b = 14.495 Å, c = 11.253 Å, β = 99.12, and V = 108.806 Å³. X-ray photoelectron spectroscopy also confirmed the +5 oxidation state vanadium in CaMgV₂O₇. The endothermic effects at 1033 and 1143 K were related to the incongruent melting and liquidus temperatures of CaMgV₂O₇, respectively. The comprehensive thermodynamic properties of CaMgV₂O₇ were established in both low- and high-temperature regions, utilizing a physical property measurement system and multi-high-temperature calorimetry (96 lines). The heat capacity (200 J mol K^?1) and entropy (198 J mol K^?1) at 298.15 K were computed based on the low-temperature heat capacity values, and the enthalpy of formation at 298.15 K was also estimated. The fitted high-temperature capacity can be used to obtain the changes in the enthalpy, entropy, and Gibbs free energy. This study is part of building a reliable thermodynamic database of the CaO–MgO–V₂O₅ system.