| Abstract: | Chemical composition, morphology, and crystalline structure of low density polyethylene (LDPE) films surface grafted with acrylic acid (AA) using corona discharge were studied by attenuated total reflection infrared (ATR-IR), electron spectroscopy for chemical analysis (ESCA), scanning electron microscopy (SEM), differential scanning calorimetry (DSC), and wide angle X-ray diffraction (WAXD) techniques. The grafted film surface is covered with grafted chains. After grafting for 3.0 h in 20% aqueous solution of AA, the depth of the grafted layer is more than 10 nm. A grain structure was observed on the grafted surfaces which was probably caused by the isolated dispersion of active sites generated by corona discharge, and these active sites initiated the graft copolymerization. However, surfaces of grafted films were smoother than that of ungrafted ones. DSC curves of grafted films show a small peak at about 100°C due to vaporization of adsorbed water. The longer the graft copolymerization time, i.e. the higher the graft degree of AA on LDPE, the higher the amount of adsorbed water. The position of each peak in WAXD patterns, crystal axial length, crystal plane distance and crystal grain size remain almost unchanged during the graft copolymerization time of 2.0 h. However, when the graft copolymerization time reaches 3.0 h, twin peaks at about 21.4° and 22.0° are observed, indicating that a different crystal form is formed at longer copolymerization time, i.e. at a higher graft degree. |