Fabrication of ambient-curable superhydrophobic fluoropolysiloxane/TiO2 nanocomposite coatings with good mechanical properties and durability
Authors:Shuxue Zhou  Xiaofeng DingLimin Wu
Affiliation:Department of Materials Science, Advanced Coatings Research Center of Ministry of Education of China, Fudan University, Shanghai 200433, China
Abstract:Ambient-curable superhydrophobic fluoropolysiloxane/TiO2 nanocomposite coatings were prepared simply by blending a hydrophobic binder with TiO2 nanoparticles. The binder consisted of triethoxysilyl-terminated fluoropolysiloxane (FPU), polymethylphenyl-siloxane (PMPS), and 3-aminopropyltriethoxysilane. The surface wettability, morphology, mechanical properties, and artificial weatherability were thoroughly investigated, using contact angle analysis, SEM, AFM, pendulum hardness rocker measurements, and nanoindentation measurements, respectively. Superhydrophobic coatings could be fabricated with FPU/PMPS weight ratios of higher than 1:9, and TiO2 loads of over 35 wt%. The superhydrophobic coatings had good mechanical strength, excellent artificial weathering durability, and resistance to organic contaminants. It was demonstrated that the TiO2 nanoparticles acted both as building blocks for the construction of the micro-/nano-structured surface, and as a photocatalyst for the decomposition of organic contaminants.
Keywords:Superhydrophobic coatings  Polysiloxane  TiO2 nanoparticles  Nanocomposite coatings  Mechanical properties  Durability
本文献已被 ScienceDirect 等数据库收录!
设为首页 | 免责声明 | 关于勤云 | 加入收藏

Copyright©北京勤云科技发展有限公司  京ICP备09084417号