The phase structure and electric properties of low-temperature sintered (K,Na)NbO3-based piezoceramics modified by CuO

0.25 wt% CuO-doped (Li,K,Na)(Nb,Ta)O₃–AgSbO₃ lead-free piezoceramics with pure perovskite structure were successfully prepared at a sintering temperature below 1000 °C. The sintering temperature of KNN-based piezoceramics was effectively reduced by about 100 °C due to the enhanced densification process induced by the addition of CuO. Besides, the acceptable sintering temperature window was broadened by the addition of CuO. It is found that the CuO-doped samples show slightly higher tetragonal–orthorhombic phase transition point (T_T−O) but a lower Curie point (T_c), compared to undoped ones. The KNN-based piezoceramics became “hard” as CuO was added, supported by an increase of Q_m. Fairly good electrical properties of d₃₃^*=383 pm/V, ε_r=860, Q_m=188 and T_c=215 °C could be obtained in dense CuO-modified KNN-based piezoceramics sintered at 970 °C, demonstrating promising potential in practical applications.