Role of Nd-Ni on structural,spectral and dielectric properties of strontium-barium based nano-sized X-type ferrites

The influence of neodymium and nickel substitution on structural and dielectric parameters was investigated in strontium-barium X-type hexagonal ferrites having composition SrBaCu_2?xNi_xNd_yFe_28?yO₄₆ (x = 0, 0.2, 0.4, 0.6, 0.8, 1 and y = 0, 0.02, 0.04, 0.06, 0.08, 0.1). Sol-gel method was employed for synthesizing these hexagonal ferrites. The XRD plots of all studied materials which were annealed at 1250 °C show single phase characteristics. Lattice parameter ‘c’ increased as a consequence of larger radius of rare earth ion (Nd³⁺) as compared to (Fe³⁺), while lattice parameter ‘a’ showed very small variation. The cell volume was obtained in the range 2508.32–2523.75 (ų). The inclusion of Nd-Ni also affected X-ray density, bulk density and porosity. The FTIR spectroscopy indicated the particular absorption peaks of hexagonal ferrites and it was performed in the range of 500–700 cm^?1. On account of Nd-Ni doping, the dielectric constant, dielectric loss and AC-conductivity showed decreasing trend. The occupancy of Nd³⁺ ions at octahedral site impedes the valence alternation of Fe³⁺; therefore there was decrease in dielectric permittivity. Ac conductivity has been decreased from 9.14 to 6.49 (Ω cm)^?1 at frequency of 2.7 GHz. The Cole-Cole plots of synthesized materials noticeably revealed grain boundary contribution. The appearance of single semi-circle in impedance Cole-Cole graphs confirms the exceptional role of grain boundaries in the conduction process. The considerably lower dielectric parameters of investigated nano X-type ferrites propose their feasibility for high-frequency applications (phase shifters, dielectric resonators, stealth technology etc).