Influence of Se and Te substitutions at Tl-site of Tl(Ba,Sr)CaCu2O7 superconductor on the AC susceptibility and electrical properties

The Sr and Ba bearing Tl-1212 phase, Tl(Ba,Sr)CaCu₂O₇ is an interesting superconductor. The Sr only bearing TlSr₂CaCu₂O₇ is not easily prepared in the superconducting form. The Ba only bearing TlBa₂CaCu₂O₇ on the other hand does not show improvement in the transition temperature with elemental substitution. In this work the influence of multivalent Se (non-metal) and Te (metalloid) substitutions at the Tl-site of Tl_1-xM_x(Ba,Sr)CaCu₂O₇ (M = Se or Te) superconductors for x = 0–0.6 was studied. The samples were prepared via the conventional solid-state reaction method. XRD patterns showed a single Tl-1212 phase for x = 0 and 0.1 Se substituted samples. The critical current density at the peak temperature, T_p of the imaginary (χ”) part of the AC susceptibility (χ = χ’ +χ”), J_c-inter(T_p) for all samples was between 15 and 21 A cm^?2. The highest superconducting transition temperature was shown by the x = 0.3 Se-substituted sample (T_c-onset = 104 K, T_c-zero = 89 K, T_cχ’ = 104 K and T_p = 80 K). Te suppressed the superconductivity of Tl-1212 phase. The order of highest transition temperatures are as follows: Tl_1-xTe_x(Ba,Sr)CaCu₂O₇<Tl(Ba,Sr)CaCu₂O₇<Tl_1-xSe_x(Ba,Sr)CaCu₂O₇. This work showed that Se was better than Te in improving the transition temperature and flux pinning of the Tl-1212 phase. The roles of ionic radius of Se and Te on the superconductivity of Tl(Ba,Sr)CaCu₂O₇ are discussed in this paper.