Influence of Y2O3 on the microstructure and tribological properties of Ti-based wear-resistant laser-clad layers on TC4 alloy

Multi-track Ti-based wear-resistant composite coatings were fabricated on TC4 alloy surfaces using laser-clad TC4 + Ni45 + Co–WC mixed powders with different Y₂O₃ contents (0, 1, and 3 wt%). The microstructure, microhardness, and tribological properties of the coatings were characterised using X-ray diffraction, scanning electron microscopy, energy dispersive spectrometry, electron probe X-ray micro analyser, microhardness tester, and friction and wear testing apparatus. The results showed that the number of cracks on the coating surfaces gradually decreased with the addition of Y₂O₃ and that residual Co–WC powders existed in the coating subsurfaces. The phase composition of the coatings with different Y₂O₃ contents remained unchanged and was mainly composed of reinforcing phases of TiC, TiB₂, Ti₂Ni, and matrix α-Ti. With the addition of Y₂O₃, the coating microstructure was remarkably refined, the direction characteristic of the TiC dendrites obviously weakened, and the nucleation rate significantly increased. When the added Y₂O₃ was 3 wt%, a large amount of TiB₂–TiC-dependent growth composite phases precipitated in the coating. The two-dimensional lattice misfit between (0001)_TiB2 and (111)_TiC was 0.912%, which indicated that TiB₂ and TiC formed a coherent interface. When the amount of Y₂O₃ was increased, the microhardness of the coatings gradually decreased, and the wear volume of the coatings first increased and then decreased. Under the effect of the TiB₂–TiC composite phases, the wear resistance of the 3 wt% Y₂O₃ coating was optimal. The 3 wt% Y₂O₃ coating friction coefficient was the lowest, and the wear mechanism was abrasive wear.