Behaviour of 54.4SiO2-13.7Na2O-1.7K2O-5.0CaO-12.4MgO-0.6Y2O3-11.3Al2O3-0.9B2O3 HT-SOFC glass sealant under oxidising and reducing atmospheres |
| |
Affiliation: | 1. Vyatka State University, Kirov, Russia;2. Institute of Solid-State Chemistry and Mechanochemistry, Siberian Branch, Russian Academy of Sciences, Novosibirsk, Russia;3. Grebenshchikov Institute of Silicate Chemistry, Russian Academy of Sciences, St. Petersburg, Russia;4. Yeltsin Ural Federal University, Yekaterinburg, Russia;5. Zavaritsky Institute of Geology and Geochemistry, Ural Branch, Russian Academy of Sciences, Yekaterinburg, Russia |
| |
Abstract: | The behaviour of the promising glass sealant 54.4SiO2-13.7Na2O-1.7K2O-5.0CaO-12.4MgO-0.6Y2O3-11.3Al2O3-0.9B2O3 for solid oxide fuel cells (SOFCs) under SOFC operating conditions was studied. First, the kinetics of the crystallisation processes at the operating temperature (850 °C) was discussed (maximum exposure time of 1000 h), and the effect of crystallisation on the coefficient of thermal expansion (CTE) of the sealant was studied. Furthermore, the degradation processes at the interface of the glass sealant and functional SOFC materials (Crofer 22 APU, YSZ, and NiO(Ni)-YSZ) during exposure to 850 °C in oxidising and reducing atmospheres for 500 h were studied. The tests demonstrated good performance of the sealant studied and possibility of its application in SOFCs. |
| |
Keywords: | Glass sealant SOFC Glass crystallisation Crystallinity Thermal compatibility Chemical stability |
本文献已被 ScienceDirect 等数据库收录! |
|