Dual functions of three-dimensional hierarchical architecture on improving the rate capability and cycle performance of LiNi0.8Co0.1Mn0.1O2 cathode material for lithium-ion battery

The main obstacles in lithium-ion battery are limited by rate performance and the rapid capacity fading of LiNi_0.8Co_0.1Mn_0.1O₂ (NCM811). Herein, a novel three-dimensional (3D) hierarchical coating material has been fabricated by in situ growing carbon nanotubes (CNTs) on the surfaces of Ni–Al double oxide (Ni–Al-LDO) sheets (named as LDO&CNT) with Ni–Al double hydroxide (Ni–Al-LDH) as both the substrate and catalyst precursor. The resultant LDO&CNT nanocomposites are uniformly coated on the surfaces of NCM811 by the physical mixing method. The rate capability of the resultant cathode material retains to 78.80% at a current rate of 3C. Its capacity retention increases by 6.7–14.42% compared with pristine NCM811 after 100 cycles within a potential range of 2.75–4.3 V at 0.5C. The improved rate capability and cycle performance of NCM811 are assigned to the synergistic effects between Ni–Al-LDO and CNTs. The hierarchical LDO&CNT nanocomposites coating on the surface of NCM811 avoids the aggregation of conductive CNTs and the stacking of Ni–Al-LDO nanosheets. Furthermore, it accelerates Li⁺ and electrons shuttle and reduces the reaction of Li₂O with H₂O and CO₂ in air, which results in Li₂CO₃ and LiOH alkali formation on the NCM811 surface.