Red-shift and improved afterglow of Sr3Al2-xBxO5Cl2:Eu2+, Dy3+ phosphors via a cation substitution strategy

Sr₃Al_2-xB_xO₅Cl₂:Eu²⁺, Dy³⁺ (x = 0, 0.2, 0.4) long persistent phosphors were prepared via solid-state process. The pristine Sr₃Al₂O₅Cl₂:Eu²⁺, Dy³⁺ phosphor exhibits orange/red broad band emission around 609 nm, which can be attributed to the electric radiation transitions 4f⁶5 d¹→4f⁷ of Eu²⁺. Upon the same excitation, the B³⁺-doped Sr₃Al_2-xB_xO₅Cl₂:Eu²⁺, Dy³⁺ phosphors display red-shift from 609 nm to 625 nm with increasing B³⁺ concentrations. The XRD patterns show that Al³⁺ can be replaced by B³⁺ in the host lattice at the tetrahedral site, which causes lattice contraction and crystal field enhancement, and thereafter achieves the red-shift on the emission spectrum. The XPS investigation provides direct evidence of the dominant 2-valent europium in the phosphor, which can be ascribed for the broad band emission of the prepared phosphors. The afterglow of all phosphors show standard double exponential decay behavior, and the afterglow of Sr₃Al₂O₅Cl₂:Eu²⁺, Dy³⁺is rather weak, while the sample co-doped with B³⁺shows longer and stronger afterglow, as confirmed after the curve simulation. The analysis of thermally stimulated luminescence showed that, when B³⁺ is introduced, a much deeper trap is created, and the density of the electron trap is also significantly increased. As a result, B³⁺ ions caused redshift and enhanced afterglow for the Sr₃Al_2-xB_xO₅Cl₂:Eu²⁺, Dy³⁺ phosphor.