| Abstract: | Studying the fragmentation law and refinement of cubic boron nitride powder under ultra-high pressure is crucial to producing a high-strength, high-density polycrystalline cubic boron nitride. In this paper, brown and black cBN crystalline powders with different micron sizes were selected as initial raw materials for an ultra-high-pressure simulation experiment. Single and mixed particles were extruded under 80MPa low pressure and 5.5GPa ultra-high pressure at ambient temperature for 1 min. The crushing behavior and particle size distribution of cBN powders with different particle sizes and ratios were investigated using a laser particle size analyzer and scanning electron microscopy. Results revealed no particle breakage or deformation at low pressure, and the compaction density was low. However, under ultra-high pressure, the cBN particles showed cracks, plastic deformation, and fragmentation, resulting in crushed fine particles filling in the voids of coarse particles, which led to a higher pressing density. Small-sized or mixed cBN particles with high density ratios were not easily crushed; the coarser the particle size, the more severe the ultra-high-pressure extrusion and crushing. The pressing density also declined, and brown cBN crystal particles with higher impact toughness demonstrated a lower particle breakage rate. The ultra-high-pressure crushing law should be considered and appropriate binders should be selected to improve the sintering performance of PcBN materials; ultra-high-pressure crushing of cBN powder contributes to cBN-cBN and cBN-M-cBN bonds under high temperatures and ultra-high pressure. |