Effect of milling ball size on the densification and optical properties of transparent Y2O3 ceramics

In this study, we report highly transparent Y₂O₃ ceramics fabricated by hot-pressing only at 1500 °C without a HIP treatment, featuring in-line transmittance levels of 77% and 84% at a wavelength of 400 and 1100 nm, respectively with the grain size suppressed to 710 nm. The effect of the ball size during the grinding of Y₂O₃ powders on the correlation between the thus-prepared Y₂O₃ powders and the optical properties of the hot-pressed samples is demonstrated for the first time. With a decrease in the diameter of the ZrO₂ balls from 5 mm to 1 mm, the milling efficiency was enhanced and admirable transparency of Y₂O₃ was attained at a short milling time. However, several micron-sized pores remained in the transparent specimens prepared with 1 mm balls, originating from the inhomogeneously packed region of the green body. Finally, the 2 mm was found to be optimum for obtaining a fine-grained and pore-free microstructure with the best in-line transmittance of Y₂O₃ ceramics.