Microstructure and electromagnetic properties of LiFe5O8 ferrite ceramics prepared from wet- and dry-milled powders

The effect of dry and wet ball milling of LiFe₅O₈ ferrite powder on the microstructure and electromagnetic properties of ferrite ceramics was studied using XRD analysis, scanning electron microscopy, dilatometry, thermogravimetry, calorimetry, and measurement of specific magnetization and electrical resistance. The sintering temperature was 1050 °C; the sintering time was 2 h. It was found that ferrite fabricated from dry-milled powder exhibits an ordered α-LiFe₅O₈ phase with bulk density of 91%. Its saturation magnetization and Curie temperature are 55 emu/g and 628°С, respectively. Specific electrical resistance is 4?10⁶ Ω cm. Wet milling in isopropyl alcohol causes formation of a disordered β-LiFe₅O₈ phase. Ceramics produced by this method shows higher bulk density (97%) and low porosity, and an order of magnitude lower resistivity. Its saturation magnetization and Curie temperature are 51 emu/g and 607°С, respectively.