Fabrication and properties of pressure-sintered reaction-bonded Si3N4 ceramics with addition of Eu2O3–MgO–Y2O3

Dense pressure-sintered reaction-bonded Si₃N₄ (PSRBSN) ceramics were obtained by a hot-press sintering method. Precursor Si powders were prepared with Eu₂O₃–MgO–Y₂O₃ sintering additive. The addition of Eu₂O₃–MgO–Y₂O₃ was shown to promote full nitridation of the Si powder. The nitrided Si₃N₄ particles had an equiaxial morphology, without whisker formation, after the Si powders doped with Eu₂O₃–MgO–Y₂O₃ were nitrided at 1400 °C for 2 h. After hot pressing, the relative density, Vickers hardness, flexural strength, and fracture toughness of the PSRBSN ceramics, with 5 wt% Eu₂O₃ doping, were 98.3 ± 0.2%, 17.8 ± 0.8 GPa, 697.0 ± 67.0 MPa, and 7.3 ± 0.3 MPa m^1/2, respectively. The thermal conductivity was 73.6 ± 0.2 W m^?1 K^?1, significantly higher than the counterpart without Eu₂O₃ doping, or with ZrO₂ doping by conventional methods.