| 重防腐涂料涂装后涂膜主要弊病分析 |
| |
| 引用本文： | 李连缀,李敏风.重防腐涂料涂装后涂膜主要弊病分析[J].电镀与涂饰,2011,30(11):68-71. |
| |
| 作者姓名： | 李连缀 李敏风 |
| |
| 作者单位： | 1. 上海振华重工(集团)股份有限公司涂料应用技术研究所,上海,201913
2. 上海斐然国际贸易公司,上海,200135 |
| |
| 摘 要： | 对重防腐涂料涂装后形成的流挂、针孔、干喷、缩孔、裂纹、发白等6种漆膜弊病的原因进行了分析,提出了预防措施和修补办法.
|
| 关 键 词： | 涂装 重防腐涂料 弊病 流挂 缩孔 |
Analysis on main faults of heavy corrosion protection paint film after coating |
| |
| LI Lian-zhui,LI Min-feng.Analysis on main faults of heavy corrosion protection paint film after coating[J].Electroplating & Finishing,2011,30(11):68-71. |
| |
| Authors: | LI Lian-zhui LI Min-feng |
| |
| Affiliation: | Institute of Coating Application Technology,Shanghai Zhenhua Heavy Industry Co.,Ltd.,Shanghai 201913,China |
| |
| Abstract: | The causes of forming six kinds of coating faults of heavy corrosion protection paint were analyzed,including sagging,pinhole,dry spraying;shrinkage,cracking,and whitening.The corresponding prevention measures and remedy were presented. |
| |
| Keywords: | coating heavy corrosion protection paint fault sagging shrinkage |