实验研究了模拟一氧化碳工业废气解毒的脱毒铬渣制备水泥矿物掺合料时,其添加比对胶砂试件抗压、抗折强度及凝结时间的影响,测定了试件中总铬（Cr）和六价铬Cr（Ⅵ）浸出浓度,并采用半动态浸出实验测定其有效扩散系数D和扩散因子L。结果表明,细磨后的脱毒铬渣符合水泥矿物掺合料的性能要求,随着添加比例的增加,胶砂凝结时间增加,抗压、抗折强度下降,但各实验组试件均达到C60的强度等级要求。试件中Cr（Ⅵ）和总Cr的D值达到10^-10~10^-9数量级,L值>9,迁移能力极低,证明制备矿物掺合料是一种安全有效的脱毒铬渣资源化处置方法。

Preparation of cement mineral admixture from chromium slag detoxified by carbon monoxide

The influence of the addition ratio of chromium slag detoxified by carbon monoxide off-gas on the compressive strength,bending strength and setting time of concrete test samples were experimentally studied.The leaching concentrations of total chromium（Cr） and hexavalent chromium Cr（Ⅵ）were determined,and their effective diffusion co-efficient D and diffu-sion factor L were calculated by semi-dynamic leaching experiment.The results showed that the detoxified chromium slag after fine grinding could meet the requirement of cement mineral admixture.With the increase of adding ratio,the setting time of mortar were extended,the compressive and bending strength were declined,but all the experimental groups meet the strength grade requirements of C60.The D value of Cr（Ⅵ） and total Cr in the sample was 10^-10~10^-9,L value was more than 9,and the migration ability was very low,which proved that the preparation of mineral admixtures was a safe and effective resource disposal method for detoxified chromium slag.