| 炭-石墨制品常见焙烧开裂现象的探究 |
| |
| 引用本文： | 杨猛,谢刚,俞小花,施辉献,钟琦.炭-石墨制品常见焙烧开裂现象的探究[J].炭素,2012(3):40-43. |
| |
| 作者姓名： | 杨猛 谢刚 俞小花 施辉献 钟琦 |
| |
| 作者单位： | 昆明理工大学冶金与能源工程学院,昆明650093 |
| |
| 摘 要： | 对冷压细颗粒制品焙烧时开裂的现象做了分析，总结出焙烧裂纹的形状，分析探讨各种裂纹产生的原因，提出防止产生焙烧裂纹的措施和方法。
|
| 关 键 词： | 炭-石墨制品 焙烧 裂纹 |
EXPLORATION TO THE COMMON CRACKING PHENOMENON ON THE CARBON GRAPHITE PRODUCTS DURING ROASTING |
| |
| Yang Meng,Xie Gang,Yu Xiao-hua,Shi Hui-xian,Zhong Qi.EXPLORATION TO THE COMMON CRACKING PHENOMENON ON THE CARBON GRAPHITE PRODUCTS DURING ROASTING[J].Carbon,2012(3):40-43. |
| |
| Authors: | Yang Meng Xie Gang Yu Xiao-hua Shi Hui-xian Zhong Qi |
| |
| Affiliation: | ( Faculty of Metallurgical and Energy Engineering, Kunming University of Science and Technology, Kunming 650093, China ) |
| |
| Abstract: | The cracking phenomenon on cold pressing fine-grained products under calcination was analyzed in this paper. The shape of the roasting crack was sumed up. The reasons of various cracks were analyzed and explored. Some measures and methods to prevent roasting crack were put forward. |
| |
| Keywords: | carbon - graphite products roasting cracking |