| 制备工艺对0.95(K_(0.5)Na_(0.5))NbO_3-0.05CaZrO_3基无铅陶瓷压电性能的影响 |
| |
| 引用本文： | 潘永军,王锋会,刘琨.制备工艺对0.95(K_(0.5)Na_(0.5))NbO_3-0.05CaZrO_3基无铅陶瓷压电性能的影响[J].陶瓷(咸阳),2014(3):24-27. |
| |
| 作者姓名： | 潘永军 王锋会 刘琨 |
| |
| 作者单位： | 西安金戈磨料磨具有限责任公司;西北工业大学工程力学系; |
| |
| 摘 要： | 采用传统陶瓷工艺制备了0.95(K0.5Na0.5)NbO3-0.05CaZrO3无铅压电陶瓷。研究了烧结温度和极化工艺对陶瓷压电性能的影响。结果表明:随着烧结温度的提高,0.95(K0.5Na0.5)NbO3-0.05CaZrO3陶瓷的体积密度增大,在1170℃时达到最大值,同时d33和kp,在此温度也分别达到他们的最大值210pC/N和0.40。极化工艺对0.95(K0.5Na0.5)NbO3-0.05CaZrO3陶瓷的压电性能有明显的影响,0.95(K0.5Na0.5)NbO3-0.05CaZrO3陶瓷的最佳极化温度是70℃,最佳极化电场是4kV/mm。
|
| 关 键 词： | 无铅压电陶瓷 铌酸钾钠 压电性能 |
Effects of Preparation Process on Piezoelectric Properties of 0.95 （ K0.5 Na0. 5 ） NbO3 - 0.05CaZrO3 Lead--free Ceramics |
| |
| Pan Yongjun,Wang Fenghui,Liu Kun.Effects of Preparation Process on Piezoelectric Properties of 0.95 （ K0.5 Na0. 5 ） NbO3 - 0.05CaZrO3 Lead--free Ceramics[J].Ceramics,2014(3):24-27. |
| |
| Authors: | Pan Yongjun Wang Fenghui Liu Kun |
| |
| Affiliation: | 1 Xi＇an Jinge Abrasives and Grinding Co. Ltd. , Xi＇an, 710600 ) ( 2 Department of Engnieering Mechanics,Northwestern Polytechnical,Xi＇an,710072) |
| |
| Abstract: | Lead-free piezoelectric ceramics 0. 95 （K0.5 Na0.5 ）NbO3- 0. 05CaZrO3were prepared by traditional ceramics process. The effect of the sintering temperature and poling conditions on piezoelectric properties of 0.95（K0. 5 Na0.5 ）NbO3 -0.05CaZrO3 ceramics was investigated. Results show that the optimum sintering temperature of 0.95 （K0. 5 Na0. 5 ）NbO3 - 0.05CaZrO3 ceramics is 1 170 ℃. Piezoelectric properties of 0.95 （K0.5 Na0.5 ）NbO3-0.05CaZrO3 ceramics under the opti- mum sintering temperature are piezoelectric constant d33 of 210 pC/N, planar electromechanical coupling factor kp of 0.40. At the same time, the results show that the optimum poling condition for 0.95 （K0. 5 Na0.5 ）NbO3 -0.05CaZrO3 ceramics is poling electric field of 4 kV/mm and poling temperature of 70℃. |
| |
| Keywords: | Lead－free piezoelectric ceramics The sintering temperature Poling condition |