| 提高连铸钢包内衬寿命的措施 |
| |
| 引用本文： | 敖进清,王怀斌,张继东,解明科.提高连铸钢包内衬寿命的措施[J].耐火材料,2000,34(4):212-213. |
| |
| 作者姓名： | 敖进清 王怀斌 张继东 解明科 |
| |
| 作者单位： | 1. 攀枝花钢铁公司钢铁研究院,攀枝花,617000
2. 攀枝花钢铁公司提钒炼钢厂 |
| |
| 摘 要： | 本文分析了攀钢钢包内衬损毁的原因。从提高耐火材料性能和使用技术两方面采取了改进措施，使钢包一次性平均使用寿命从72次提高到90次，最高达115次，取得了显著的经济效益。
|
| 关 键 词： | 连铸钢包，使用寿命 |
| 修稿时间： | 2000-01-12 |
Measures for extending lining life of continuous casting ladle |
| |
| Ao Jinqing
,Wang Huaibin
,Zhang Jidong.Measures for extending lining life of continuous casting ladle[J].Refractories,2000,34(4):212-213. |
| |
| Authors: | Ao Jinqing Wang Huaibin Zhang Jidong |
| |
| Affiliation: | Ao Jinqing
,Wang Huaibin
,Zhang Jidong
;(Iron & Steel Institute, Panzhihua Iron & Steel Company, Panzhihua 617000) |
| |
| Abstract: | Corrosion reason of the ladle lining of Panzhihua Iron and Steel Company was analyzed. The improving measures were taken based on optimizing the properties of refractories and improving application technology. The average service life of the ladle without repair increased from 72 heats to 90 heats, the highest reaches 115 heats. |
| |
| Keywords: | Continuous casting ladle Service life |