Research of laser remelting on the thermal-mechanical behaviors and heat treatment of yttria-stabilized zirconia coatings |
| |
Authors: | Peng Yi Xiaoye Zhu Yongliang Jiang Wenlong Feng Zhihao Feng Yanchao Jin Guixin Dong |
| |
Affiliation: | College of Mechanical and Electronic Engineering, China University of Petroleum, Qingdao, China |
| |
Abstract: | In this study, the thermal and mechanical behaviors were investigated by simulating laser remelting of atmospheric plasma-sprayed yttria-stabilized zirconia coatings, and the molten depth and regions of stress concentration were compared between simulation and experiment. The heat treatment process of the remelted coating was also simulated. The crack formation mechanism in the YSZ coating remelted by laser and the heat-treatment effect on residual stress were investigated. Results showed that the simulated results were consistent with the experimental measurements, and the residual thermal stress was the main cause of cracks formation. The coating remelted by a laser power of 1500 W and a scanning rate of 9 mm/s possessed less residual concentrated stress and segmented cracks. Heat treatment released concentrated stress, which was still accurate for the ceramic coating. If the coatings were slowly heated to demonstrate heat treatment after laser remelting, the cracks in the remelted layer decreased correspondingly. |
| |
Keywords: | heat treatment laser remelting thermal and mechanical behaviors thermal barrier coatings |
|
|