Hybrid polymer matrix composite (UHMWPE-HPMC) as solid particle erosion resistant coating for sharp pipe elbows using numerical simulation and experimental analysis

A hybrid polymer matrix composite coating, resistant to solid particle erosion inside sharp elbows, consisting interlocking chains of molecules with the ability to deflect the surface impact stress and to uniformly distribute stresses along the hard-ceramic reinforcement mixture surface was developed. Formulated mixture of ceramic reinforcement particles mixtures (alumina, tungsten carbide, and silicon carbide) with polymer coupling agents; to increase adhesion to the metal surface, led to 600–700 HVN in ternary and 500–550 HVN in binary mixtures. This behavior coincides with high shear strength of 70–76 MPa, Young's and shear modulus of 8.86 and 13.4 GPa in ternary 15%Al₂O₃-5%WC-10%SiC, respectively. The low erosion weight loss of 0.1% and small coefficient of friction near 0.18 indicates the significant wear resistance of the ternary sample. The electron microscopic micrographs determined the dense smooth coating surfaces with adhesive interfaces with the substrate.