ZrO2(3Y)包裹Al2O3纳米复合粉体的制备
引用本文:杨建,刘姣,丘泰,林洁. ZrO2(3Y)包裹Al2O3纳米复合粉体的制备[J]. 化工学报, 2006, 57(8): 1997-2001
作者姓名:杨建  刘姣  丘泰  林洁
作者单位:南京工业大学材料科学与工程学院,江苏,南京,210009;南京工业大学材料科学与工程学院,江苏,南京,210009;南京工业大学材料科学与工程学院,江苏,南京,210009;南京工业大学材料科学与工程学院,江苏,南京,210009
摘    要:以pH值缓冲溶液为沉淀剂,用非均匀成核和液相共沉淀相结合的方法合成出了ZrO2(3Y)包裹Al2O3纳米复合粉体.用XRD、TEM对所制备粉体进行了表征.研究表明:加入分散剂使Al2O3悬浮液的等电点向酸性区移动,Zeta电位绝对值增大,其中pH值为9.56对应的Zeta电位绝对值最大,悬浮液最稳定.Al2O3悬浮液pH值为9.5,ZrOCl2和YCl3混合溶液浓度为0.2 mol•L-1时前驱体的收得率最高.600℃煅烧后得到的粉体中只有α-Al2O3、t-ZrO2两种物相,在Al2O3颗粒表面附着10 nm左右的ZrO2(3Y)颗粒.

关 键 词:非均匀成核  ZrO2(3Y)包裹Al2O3  纳米复合粉体
文章编号:0438-1157(2006)08-1997-05
收稿时间:2005-12-26
修稿时间:2005-12-262006-04-27

Preparation of ZrO2(3Y)encapsulated Al2O3 nanometer composite powders
YANG Jian,LIU Jiao,QIU Tai,LIN Jie. Preparation of ZrO2(3Y)encapsulated Al2O3 nanometer composite powders[J]. Journal of Chemical Industry and Engineering(China), 2006, 57(8): 1997-2001
Authors:YANG Jian  LIU Jiao  QIU Tai  LIN Jie
Abstract:ZrO2(3Y)encapsulated Al2O3 nano composite powders were prepared by heterogeneous nucleation combined with the liquid co-deposition method using pH buffer solution as precipitator.The synthesized powders were characterized with XRD and TEM.The results indicated that the isoelectric point of Al2O3 suspension shifted to acidic side and the absolute value of Zeta potential also increased when a dispersant was added into the suspension.At pH 9.56,the absolute value of Zeta potential reached the maximum and the suspension was most stable.The maximum yield of the precursor was obtained at pH 9.5 and the concentration of ZrOCl2and YCl3mixed solution 0.2 mol•L-1.There existed two phases,i.e.,α-Al2O3 and t-ZrO2,in the composite powders calcined at 600℃.TEM observation confirmed that nano ZrO2(3Y)particles with a diameter of 10 nm were formed on the surface of Al2O3 particles.
Keywords:heterogeneous nucleation  ZrO_2(3Y)encapsalated Al_2O_3  nano composite powders  