Effects of (Li0.5Sm0.5)/W co-substitution and sintering temperature on the structure and electrical properties of ultrahigh Curie temperature piezoceramics,Ca0.92(Li0.5Sm0.5)0.08Bi2Nb2-xWxO9 |
| |
| Authors: | Changbai Long Ning Ji Li Yang Wenjie Zhou Kun Zheng Wei Ren Laijun Liu |
| |
| Affiliation: | 1. School of Advanced Materials and Nanotechnology, Xidian University, Xi’an, 710071, China;2. Key Laboratory of New Processing Technology for Nonferrous Metal & Materials, Ministry of Education/ Guangxi Key Laboratory of Optical and Electronic Materials and Devices, Guilin University of Technology, Guilin, 541004, China;3. Electronic Material Research Laboratory, Key Laboratory of the Ministry of Education & International Center for Dielectric Research, Xi’an Jiaotong University, Xi’an, 710049, China |
| |
| Abstract: | With co-substitution of (Li0.5Sm0.5) at A site and W at B site, the electrical properties of modified Ca0.92(Li0.5Sm0.5)0.08Bi2Nb2-xWxO9 (CLS)BN-xW, x = 0, 0.015 and 0.03] piezoceramics with ultrahigh Curie temperature (TC) of > 930 °C were enhanced dramatically. The increased resistivity induced by the co-substitution ensure them to be polarized under an enough high field. Combined with the increase of spontaneous ferroelectric polarization (PS), the significant enhancements in the piezoelectric, dielectric and ferroelectric properties can be obtained in the composition x = 0.015. Furthermore, the piezoelectric activity (d33) and bulk resistivity (ρb) of (CLS)BN-0.015 W can be further enhanced at an appropriate sintering temperature. This optimum composition sintered at 1170 °C shows ultrahigh TC of ～948 °C, d33 of ～17.3 pC/N and ρb of ～6.9 MΩ cm at 600 °C, which are comparable to those of the reported high-temperature Aurivillius piezoceramics with TC > 850 °C. |
| |
| Keywords: | Aurivillius-phase piezoceramics Ultrahigh curie temperature Sintering temperature Electrical properties |
| 本文献已被 ScienceDirect 等数据库收录！ |
|