Optical and thermo-mechanical properties of fine-grained transparent yttria ceramics fabricated by hot-press sintering for infrared window applications

In this work, highly transparent yttria ceramics Φ?=?55?mm in size were fabricated by a hot-pressing method with 1 at.% ZrO₂ or 12 at.% La₂O₃ as a sintering additive. For a 4-mm-thick specimen doped with ZrO₂, the in-line transmittance reaches 71.1% at 400?nm and 80.9% at 1100?nm, and the transmittance of the La₂O₃-doped specimen is comparable to that of the ZrO₂-doped specimen. By means of the relatively low sintering temperature of 1600?°C, the present samples exhibited very fine microstructures (<2?μm), giving rise to excellent mechanical strength levels (～200?MPa). With regard to the 1 at.% ZrO₂-doped specimen, the combination of high strength and high thermal conductivity (～10 W/m?K) substantially improved parameters related to the thermal shock resistance. The results of this study indicate that the hot-pressed transparent yttria ceramic doped with 1 at.% ZrO₂ is optically, mechanically, and thermally suitable for high-temperature IR window applications.