Effects of anion and cation doping on the thermoelectric properties of n-type PbS

The PbCl_xS_1-x and Pb_1-xBi_xS (x? =?0–0.05) bulks were fabricated with a facile method of hydrothermal synthesis and microwave sintering, and the effect of anionic and cationic donors on the thermoelectric performance of PbS was investigated. Although Cl^? and Bi³⁺ both effectively improved the thermoelectric properties of n-type PbS, more excellent thermoelectric performance was obtained from Cl^? doped samples because of higher electrical property and lower thermal conductivity at higher temperature (T? >?600?K). The thermoelectric figure of merit (ZT) reaches 1.04 for PbCl_0.015S_0.985 at 800?K and increases with temperature increasing without sign of saturation, which is probably the highest value ever reported for single-phase polycrystalline n-type PbS. The results also indicate that the hydrothermal synthesis and microwave sintering can realize anion doping as well as cation doping for n-type PbS at low cost, and PbS should be a robust alternative for PbTe thermoelectric materials.