| 烷基化氢氟酸工艺管道焊缝伪裂纹成因分析 |
| |
| 引用本文： | 陈江,娄忆清,包士毅.烷基化氢氟酸工艺管道焊缝伪裂纹成因分析[J].浙江工业大学学报,2000,28(2):95-98. |
| |
| 作者姓名： | 陈江 娄忆清 包士毅 |
| |
| 作者单位： | 浙江工业大学机电工程学院!浙江杭州310032 |
| |
| 摘 要： | 分析了烷基化氢氟酸工艺管道的腐蚀行为，年了在Ｘ射线拍片中含裂纹状影象的氢氟酸工艺管道焊缝，阐述了焊缝伪裂纹产生原因。
|
| 关 键 词： | 工艺管道 缺陷 应力腐蚀 炼油厂 焊缝 |
| 修稿时间： | 2000-01-16 |
Cause analysis of bogus cracks in weld of hydrofluoric acid pipelines in alkyl procedure |
| |
| CHEN Jiang,LOU Yi\|qing,BAO Shi\|yi.Cause analysis of bogus cracks in weld of hydrofluoric acid pipelines in alkyl procedure[J].Journal of Zhejiang University of Technology,2000,28(2):95-98. |
| |
| Authors: | CHEN Jiang LOU Yi\|qing BAO Shi\|yi |
| |
| Abstract: | The
corrosion behaviour of hydrofluoric acid pipelines in alkyl procedure is analysed. The
pipeline welds of which the X-ray photographs contain images like crack image are
sectioned and the cause of bogus cracks is explained. |
| |
| Keywords: | pipeline crack assessment stress corrosion corrosion |
| 本文献已被 CNKI 维普 万方数据 等数据库收录！ |