| 介孔二氧化钛的制备及其光催化性能 |
| |
| 引用本文： | 何秀,程宝箴,孙冬兰,王小聪.介孔二氧化钛的制备及其光催化性能[J].天津轻工业学院学报,2013(6):24-27. |
| |
| 作者姓名： | 何秀 程宝箴 孙冬兰 王小聪 |
| |
| 作者单位： | [1]天津科技大学材料科学与化学工程学院,天津300457 [2]天津科技大学理学院,天津300457 |
| |
| 基金项目： | 天津市生物医学材料重点实验室开放课题（20120201）;天津科技大学实验室开放基金项目（1111A218） |
| |
| 摘 要： | 以异丙醇钛为前躯体，十六烷基三甲基溴化铵为模板剂，采用溶胶一凝胶法合成介孔二氧化钛．通过X射线粉末衍射、扫描电子显微镜、透射电子显微镜、比表面积测定仪对样品进行表征．以亚甲基蓝溶液为光催化降解对象，研究二氧化钛用量及不同模板剂对光催化性能的影响．实验结果表明：当催化剂用量在0．50g／L时，反应4h后亚甲基蓝的降解率可达到99．1％；在3种模板剂中，以十六烷三甲基溴化铵为模板剂合成的介孔二氧化钛光催化效果最好
|
| 关 键 词： | 介孔二氧化钛 模板剂 光催化 亚甲基蓝 |
Preparation of Mesoporous Titania and its Photocatalytic Performance |
| |
| HE Xiu,CHENG Baozhen,SUN Donglan,WANG Xiaocong.Preparation of Mesoporous Titania and its Photocatalytic Performance[J].Journal of Tianjin University of Light Industry,2013(6):24-27. |
| |
| Authors: | HE Xiu CHENG Baozhen SUN Donglan WANG Xiaocong |
| |
| Affiliation: | 1. College of Material Science and Chemical Engineering, Tianjin University of Science ＆ Technology, Tianjin 300457, China; 2. College of Science, Tianjin University of Science ＆ Technology, Tianjin 300457, China) |
| |
| Abstract: | Mesoporous titania was synthesized via a sol-gel method by using isopropyl titanate as the precursor and cetyl trimethyl ammonium bromide as the template. X-ray diffraction （XRD）, scanning electron microscope （SEM）, transmission electron microscope （TEM） and BET surface area measurement were used to characterize the product. Methyl blue was used as the object of photocatalytie degradation, and the influence of TiO2 dosage and different kinds of template on the photo- catalytic performance was studied. The result indicated that the degradation rate of methyl blue could reached 99.1% within 4 h when the amount of catalyst was 0.50 g/L. Preparation of mesoporous titania using cetyl trimethyl ammonium bromide as template gave the best photocatalytic activity among the three kinds of template. |
| |
| Keywords: | mesoporous titania template photocatalysis methyl blue |