| Damage Mechanism of Al2O3 Ceramic Coatings Irradiated by CO2 CW Laser |
| |
| 作者姓名： | 李东荣 王富耻 马壮 王全胜 柳彦博 |
| |
| 作者单位： | School of Material Science and Engineering Beijing Institute of Technology，School of Material Science and Engineering，Beijing Institute of Technology，School of Material Science and Engineering，Beijing Institute of Technology，School of Material Science and Engineering，Beijing Institute of Technology，School of Material Science and Engineering，Beijing Institute of Technology，Beijing 100081，China，Beijing 100081，China，Beijing 100081，China，Beijing 100081，China，Beijing 100081，China |
| |
| 基金项目： | Ministerial Level Advanced Research Foundation |
| |
| 摘 要： | Rules and mechanism of damage in Al2O3 coatings irradiated by CO2 CW laser are studied in order to improve the ability of parts of equipment standing against the high power laser.Al2O3 coatings were sprayed by air plasma spray(APS)on the 45# steel substrate,and then were irradiated by CO2 CW laser from 795 W/cm2 to 31 830 W/cm2.As the output power of the laser is increasing,its porosity is increasing and cracks are appearing and spreading quickly.And also the phase will transform from γ-Al2O3 to α-Al2O3 in the damaged areas.When the energy density is 17 507 W/cm2,the coatings are destroyed completely.The thermal infection field on substrate is rather small.The laser energy is depleted by the phase transformation and cracks in Al2O3 coatings during the laser thermal shock.
|
| 关 键 词： | CW激光器 等离子喷雾 三氧化铝覆层 损害原理 |
Damage Mechanism of Al2O3 Ceramic Coatings Irradiated by CO2 CW Laser |
| |
| LI Dong-rong,WANG Fu-chi,MA Zhuang,WANG Quan-sheng and LIU Yan-bo.Damage Mechanism of Al2O3 Ceramic Coatings Irradiated by CO2 CW Laser[J].Journal of Beijing Institute of Technology,2008,17(2):227-231. |
| |
| Authors: | LI Dong-rong WANG Fu-chi MA Zhuang WANG Quan-sheng and LIU Yan-bo |
| |
| Affiliation: | School of Material Science and Engineering, Beijing Institute of Technology, Beijing 100081, China |
| |
| Abstract: | Rules and mechanism of damage in Al2O3 coatings irradiated by CO2 CW laser are studied in order to improve the ability of parts of equipment standing against the high power laser. Al2O3 coatings were sprayed by air plasma spray(APS) on the 45# steel substrate, and then were irradiated by CO2 CW laser from 795W/cm2 to 31830W/cm2. As the output power of the laser is increasing, its porosity is increasing and cracks are appearing and spreading quickly. And also the phase will transform from γ-Al2O3 to α-Al2O3 in the damaged areas. When the energy density is 17507W/cm2, the coatings are destroyed completely. The thermal infection field on substrate is rather small. The laser energy is depleted by the phase transformation and cracks in Al2O3 coatings during the laser thermal shock. |
| |
| Keywords: | CW laser plasma spray Al2O3 coatings demolishment |