丁二烯聚合中铁系催化剂烷基铝作用的研究

研究了在２５℃加氢汽油介质中，铁系胶体催化剂［Ｆｅ（ｎａｐｈ）２ Ａｌ（ｉ Ｂｕ）３ ＣＨ２＝ＣＨＣＨ２Ｃｌ］单组分、多组分按不同配比混合，非水体系电导率与浓度的关系，结合Ｔｙｎｄａｌ效应，聚合实验结果，得出Ａｌ（ｉ Ｂｕ）３以缔合状态存在并解离成离子对；它同环烷酸亚铁的作用是形成胶核的主要反应；与氯丙烯反应生成的氯化异丁基铝，在胶核表面参与形成活性中心；由过量Ａｌ（ｉ Ｂｕ）３解离的离子对形成的双电层结构，使胶粒保持相对稳定。催化剂各组分较佳配比对应稳定胶粒的形成；它具有颗粒小、均匀、较高的催化活性。催化体系加入丁二烯引起电导率下降表明活性中心是正离子性的。

Function of Aluminum Alky for Butadiene Polymerization with Alkyl Iron Catalyst System

The　relationship　was　studied　between　nonaqueous　system　electroconductivity　of　single　component　and　multi component　mixed　by　different　ratios　of　iron　system　colloidal　catalyst　Fe(naph)_2-Al(i-Bu)_3-CH_2-CHCH_2Cl]　and　their　concentration　in　hydrogenated　gasoline　medium　at　25℃.And　through　Tyndall　effect　and　polymerization　experiment　Al(i-Bu)_3　existed　in　associate　state　and　was　dissociated　into　ionpair.The　reaction　between　Al(i-Bu)_3　and　Fe(naph)_2　was　the　main　reaction　which　formed　colloidal　core;while　it　reacted　with　chlorallylene,AIR4CH2=CHCH2Cl　was　yielded,it　joined　in　the　formation　of　active　center　on　the　surface　of　colloidal　core.The　excessive　Al(i-Bu)_3　was　dissociated　into　ionpair　forming　a　double　electrode　layer,and　the　layer　kept　the　colloidal　particles　relatively　stable.The　optimal　component　tatios　of　catalyst　corresponded　with　the　forming　of　stable　colloidal　particles　which　was　tiny,uniform　and　of　high　catalytic　activity.While　butadiene　was　added　to　the　catalytic　system　the　electroconductivity　was　reduced.It　showd　that　the　active　center　was　positive　ionicity.