纸纤维基柔性还原氧化石墨烯、聚苯胺超级电容器复合电极材料的制备与性能研究

文章研究了一种石墨烯复合电极材料制备方法，以低成本的纸纤维材料为柔性基板，结合双电层电容碳材料氧化石墨烯和赝电容导电聚合物聚苯胺的互补优势，通过超声分散和真空抽滤的方法，实现了纸纤维基-聚苯胺-还原氧化石墨烯复合电极材料的制备。采用场发射扫描电子显微镜、Zahner电化学工作站对电极材料的循环伏安曲线、充放电性能进行测试分析。结果表明，柔性电极材料在100次弯曲测试后，没有发生明显分层和活性物质剥落现象，在电流密度为1 A/g时比电容为458 F/g，10 A/g电流密度下比电容为250 F/g，经过1000次充放电循环后，比电容仍能保持80%左右。这种高性能低成本的柔性复合电极材料在可穿戴式电子设备领域具有广阔的应用前景。

Preparation and Study of the Paper Fiber-Based Flexible Supercapacitors Electrode with Reduced Graphene Oxide and Polyaniline Hybrid Materials

A flexible paper fiber-reduced graphene oxide-polyaniline hybrid electrode was investigated in this article. Using low-cost paper fiber as flexible substrate, the electrode was prepared through ultrasonic dispersion and vacuum filtration. It combined the advantages of graphene oxide electric double layer with polyaniline conductive polymer pseudo-capacitance. The obtained electrode was characterized and tested by various instrumentations such as scanning electron microscope, cyclic voltammetry and galvanostatic charge-discharge. In the bending test experiments, the obtained electrode was not separated into individual layers after hundreds of bending cycles. The lfexible paper ifber-reduced graphene oxide-polyaniline hybrid electrode also exhibits excellent capacitance (458 F/g at a discharge current density of 1 A/g and 250 F/g at a discharge current density of 10 A/g) and remarkable cycling stability with capacitance degradation about 20%after 1 000 charge-discharge cycles at a current density of 3 A/g. The proposed lfexible electrode has great potentials in the development of lfexible energy-storage devices for wearable electronic products.