| Abstract: | Surface pretreatment for adhesive bonding of aluminum with adhesive mediator The influence of three steps pretreatment degreasing, blasting and primer and the two steps pretreatment degreasing and blasting on the adhesive behaviour of aluminum alloy AlMg4,5Mn0,5 were investigated. The investigations were preformed using two cold hardening two‐components epoxy adhesives, one hot hardening one‐component epoxy adhesive and one cold hardening two‐components polyurethane adhesive. The three steps pretreatment indicate that the adhesion bonding strength by epoxy adhesives are higher than that by two steps pretreatment. On the other hand, the adhesion bonding strength was similar by using polyurethane adhesive independence of the pretreatment method. Leaving out the pretreatment step degreasing after corund blasting caused by using, PU, EP 2 and EP 3 adhesives a significant decreasing of the bonding strength in comparison with the only degreased specimen. This degreasing process was used to remove the residual blasting medium from the aluminum surfaces after blasting. The topographical structure of the surfaces after corund blasting was covered by further pretreatment with primer as a consequence of higher primer viscosity, which causes a decreasing in the surface roughness. The chemical composition of pretreated surfaces by three steps was different from that by two steps. |