| Abstract: | To gain insight into the ageing behavior of ultrafine grain(UFG)structure,the precipitation phenom-ena and microstructural evolutions of Mg-6Zn-1Y-0.4Ce-0.5 Zr(wt.％)alloy processed by sliding friction treatment(SFT)were systematically studied using hardness texting,transmission electron microscopy(TEM)equipped with high-angle annular dark-field scanning(HADDF-STEM),X-ray diffraction(XRD)and XRD line broadening analysis.The microhardness of the SFT-processed(SFTed)sample initially decreases from 109.6 HV to 104.8 HV at ageing for 8 h,and then increases to the peak-ageing point of 115.4 HV at 16 h.Subsequently,it enters the over-aged period.The un-SFTed sample,as the counterpart,follows a regular ageing behavior that increases from 89.9 HV to 99.6 HV when ageing for 12 h,and then drops.A multi-mechanistic model is established to describe the strengthening due to grain refinement,disloca-tion accumulation,precipitation etc.The analysis reveals that the temperature sensitive UFG structure has an obvious grain coarsening effect,which arouses the soft phenomenon in the early ageing stage.But precipitation hardening provides an excellent hardness enhancement for overcoming the negative influ-ence and helping to reach the peak-aged point.In our microstructural observations,a lot of equilibrium ultrafine MgZn2 precipitates precipitate along dislocations because defects can provide the favorable conditions for the migration and segregation of solute atoms. |