Electrical properties of Pb(Mg1/3Nb2/3)O3-PbTiO3 ceramics modified with WO3

Ferroelectrics 0.67Pb (Mg_1/3Nb_2/3)O₃-0.33PbTiO₃ (PMN-PT) + x mol% WO₃ (x=0.1, 0.5, 1, 2) were prepared by columbite precursor method. Electrical properties of WO₃-modified ferroelectrics were investigated. X-ray diffraction (XRD) was used to identify crystal structure, and pyrochlore phase were observed in 0.67Pb (Mg_1/3Nb_2/3)O₃-0.33PbTiO₃+2 mol% WO₃. Dielectric peak temperature decreased with WO₃ doping, indicating that W⁶⁺ incorporated into PMN-PT lattice. Lattice constant, pyrochlore phase and grain size contribute to the variation of K_max. Both piezoelectric constant (d₃₃) and electromechanical coupling factors (k_p) were enhanced by doping 0.1 mol% WO₃, which results from the introduction of “soft” characteristics into PMN-PT, while further WO₃ addition was detrimental. We consider that the two factors, introduction of “soft” characteristics and the formation of pyrochlore phase, appear to act together to cause the variation of piezoelectric properties of 0.67PMN-0.33PT ceramics doping with WO₃.