TiC-xNi金属陶瓷的燃烧合成及其热物理性能

利用自蔓延高温燃烧民结合机械厂压力方法制备了TiC-Ni金属陶瓷，研究了ＴiC-Ni金属陶瓷材料的密度，比热度、比热容、热传导以及热膨胀性质随温度和组成的变化关系，结果表明：ＴiC-Ni材料的密度在w(Ni)为２０％时致密性达到最高，材料的比定压热容在浊试温度区内呈线性增加；ＴiC-Ni材料的热扩散率随度的升高基本呈增加趋势，热扩散率随Ｎi含量的增加而增加，热导率的变化与热扩散率的变化有相似的规律，材料的热膨胀系数随温度的升高单调递增，温度上升相同情况下，材料的热膨胀系数随Ｎi含量的增加而增加。

Thermal physical properties of TiC-xNi cermets produced by combustion synthesis

Presents the preparation of TiC-Ni cermets by combining forced compaction with self propagating high temperature synthesis (SHS), the investigation of the density, specific heat, thermal diffusivity, thermal conductivity and thermal expansion coefficient of TiC-Ni cermets at different temperatures and constitutes and concludes that TiC-Ni cermets gained the maximum density when Ni content is 20wt%; Specific heat increased with temperature at testing temperature, but it changed not too much; thermal diffusivity trended to increase with temperature and Ni content nearly, which is the similar to thermal conductivity; thermal expansion coefficient of TiC-Ni cermets increased monotonously with temperature increasing, and also increased with Ni content when the cermets were heated to the same temperature.