轧制温度和累积应变对累积叠轧焊AZ31镁合金板材组织和性能的影响

通过光学显微镜（OM）、扫描电镜（SEM）和力学性能检测，研究了AZ31镁合金在不同温度和累积应变条件下累积叠轧后的微观组织和力学性能。结果表明：晶粒尺寸随累积叠轧温度降低和累积应变增加而减小；经过3道次的ARB变形后，晶粒细化不再显著，但是组织均匀性得到改善。300℃以上的ARB变形对AZ31板材的强度和延性均有一定...

Effect of the Rolling Temperature and Accumulated Strain on the Microstructure and Mechanical Properties of AZ31 Alloy Sheet by Accumulative Roll-bonding

Accumulative roll-bonding(ARB) was applied to AZ31 magnesium alloy at various rolling temperatures and cycles.The microstructures and mechanical properties of ARBed AZ31 alloys were investigated.The results show that the grain sizes decrease with decreasing of the rolling temperatures and increasing of ARB cycles.The grain refining is prominent until three cycles and the microstructures become more homogeneous with increasing of ARB cycles.The changes in tensile strength and ductility are more complicated as a result of the combined effects of the temperature and accumulated strain on grain size,texture and interface bonding.The best compromise between the strength and ductility is obtained after ARB at 350℃for three cycles.The average ultimate tensile strength is 277 MPa and average tensile elongation is 20.6%which can be further improved after annealing.