| Mg掺杂ZnO纳米棒阵列的场发射性能研究 |
| |
| 引用本文： | 叶芸,;刘玉会,;张典,;陈丽雯,;郭太良,;蒋亚东.Mg掺杂ZnO纳米棒阵列的场发射性能研究[J].纳米技术与精密工程,2014(4):269-274. |
| |
| 作者姓名： | 叶芸 ;刘玉会 ;张典 ;陈丽雯 ;郭太良 ;蒋亚东 |
| |
| 作者单位： | [1]福州大学物理与信息工程学院,福州350002; [2]电子科技大学电子薄膜与集成器件国家重点实验室,成都610054 |
| |
| 基金项目： | 国家高技术研究发展计划（863计划）资助项目（2013AA030601）;国家自然科学基金资助项目（61106053,61101169）;电子薄膜与集成器件国家重点实验室开放基金资助项目（KFJJ201309）. |
| |
| 摘 要： | 采用水热法在硝酸锌(Zn(NO3)2·6H2O)与硝酸镁(Mg(NO3)2·6H2O)的生长液中制备了Mg掺杂的Mg/ZnO(MZO)纳米棒,其中生长液中Mg2+的物质的量浓度c(Mg2+)分别为0.05 mol/L、0.10 mol/L、0.25 mol/L和0.50 mol/L.利用场发射电子显微镜(FESEM)、X射线光电子能谱仪(XPS)、X射线衍射仪(XRD)、光致发光谱(PL)测试及场发射测试对所制备的MZO纳米棒的表面形貌、成分、晶体结构、光学性能及场发射性能进行了研究.结果表明:随着生长液中c(Mg2+)的增加,MZO纳米棒的直径逐渐减小、缺陷逐渐增加;且掺入的Mg含量与c(Mg2+)并不成正比关系;当生长液中的c(Mg2+)为0.10 mol/L时,所制备的MZO纳米棒的场发射性能最好,其开启场强为2.85 V/μm.
|
| 关 键 词： | Mg掺杂 MZO纳米棒 水热法 场发射 |
Field Emission Properties of Mg Doped ZnO Nanorod Arrays |
| |
| Affiliation: | Ye Yun, Liu Yuhui, Zhang Dian , Chen Liwen , Guo Tailiang , Jiang Yadong (1. College of Physics and Telecommunication Engineering, Fuzhou University, Fuzhou 350002, China; 2. State Key Laboratory of Electronic Thin Films and Integrated Devices, University of Electronic Science and Technology of China, Chengdu 610054, China) |
| |
| Abstract: | Mg-doped ZnO （MZO） nanorod arrays were fabricated by hydrothermal method in the mixedsolution of Zn（ NO3 ）·6H2O and Mg（ NO3 ）2 ·6H2O with Mg2＋ concentrations varying from 0. 05 mol/L,0. 10 mol/L, 0.25 mol/L to 0.50 mol/L. The morphology and composition of MZO arrays were charac-terized by field emission scanning electron microscopy （FESEM） and X-ray photoelectron spectroscopy（XPS）, respectively. The effects of Mg dopants on the crystal structures and optical properties were in-vestigated by using X-ray diffraction（XRD） and photoluminescence（ PL）, then their field emission prop-erties were also evaluated. Results show that higher doping led to the formation of nanorod arrays withsmaller diameters and more defects, but the higher c （ Mg2 ＋ ） in solution did not induce higher Mg doping.The best field emission performance of the MZO nanorod arrays was synthesized in 0. 10 mol/L c（ Mg2＋ ）solution, which had a low turn-on field of 2. 85 V/μm. |
| |
| Keywords: | Mg doping MZO nanorod hydrothermal method field emission |