Effect of stirring on the dissolution of coal fly ash and synthesis of pure-form Na-A and -X zeolites by two-step process

Using the coal fly ash (FA), pure-form Na-A and -X zeolites were synthesized by two-step process. The FA was pretreated in aqueous NaOH solution under stirring condition at 85 °C for 18 h. The amorphous aluminosilicate of FA was dissolved during pretreatment. Increasing the stirring speed accelerated the dissolution of FA and increased Si⁴⁺ and Al³⁺ concentrations in the solution. This fact indicated that the stirring during pretreatment significantly affected on the dissolution of FA. After pretreatment, remaining FA was removed and aqueous NaAlO₂ solution was added to the residual solution to control the molar ratio SiO₂/Al₂O₃ of 0.5–4.5. After aging the resultant at 85 °C for 24 h, white precipitates were generated over the whole SiO₂/Al₂O₃ range. Increment of Si⁴⁺ concentration by stirring during pretreatment increases the yield of the product. At SiO₂/Al₂O₃ = 0.5, the material was identified as Na-A zeolite with a trace amount of hydroxysodalite. A single phase Na-A zeolite was obtained at SiO₂/Al₂O₃ = 1.0. The Na-X zeolite was emerged at SiO₂/Al₂O₃ ? 2.0. At SiO₂/Al₂O₃ = 4.5, a single phase Na-X zeolite was formed. The cation exchange capacity of synthetic single phase Na-A and -X zeolites was respectively 4.78 and 3.88 meq./g.