| 工艺参数对316不锈钢粉末激光烧结球化的影响 |
| |
| 引用本文： | 潘琰峰,沈以赴,顾冬冬,杨家林,王洋.工艺参数对316不锈钢粉末激光烧结球化的影响[J].材料工程,2005(5):52-55. |
| |
| 作者姓名： | 潘琰峰 沈以赴 顾冬冬 杨家林 王洋 |
| |
| 作者单位： | 1. 南京航空航天大学,南京,210016
2. 中国工程物理研究院,四川,绵阳,621900 |
| |
| 基金项目： | 国家自然科学基金
,
中国工程物理研究院联合基金
,
南京航空航天大学校科研和教改项目 |
| |
| 摘 要： | 采用直接金属激光烧结的方法,对316不锈钢粉末进行了一系列烧结实验.实验发现,在液相粘度较高、表面张力大,熔体材料不浸润固相颗粒和基板等因素的影响下,烧结过程中出现了球化现象.球化的出现妨碍了直接金属激光烧结成形的顺利进行.分析了316不锈钢粉末球化效应产生的原因,讨论了工艺参数(激光功率、扫描速度和粉层厚度)对316不锈钢金属粉末烧结成形的影响.研究表明,适当提高扫描速度或减小激光功率可以在一定程度上减小316不锈钢粉末激光烧结的球化效应.
|
| 关 键 词： | 直接金属激光烧结 金属粉末 球化效应 工艺参数 工艺参数 不锈钢 金属粉末 激光烧结成形 球化效应 影响 Stainless Steel Powders Sintering Laser Direct During Process Parameters 程度 研究 粉层厚度 扫描速度 激光功率 分析 现象 烧结过程 |
| 文章编号： | 1001-4381(2005)05-0052-04 |
| 修稿时间： | 2004年11月8日 |
Effect of Process Parameters on Balling During Direct Laser Sintering of 316 Stainless Steel Powders |
| |
| PAN Yan-feng,SHEN Yi-fu,GU Dong-dong,YANG Jia-lin,WANG Yang.Effect of Process Parameters on Balling During Direct Laser Sintering of 316 Stainless Steel Powders[J].Journal of Materials Engineering,2005(5):52-55. |
| |
| Authors: | PAN Yan-feng SHEN Yi-fu GU Dong-dong YANG Jia-lin WANG Yang |
| |
| Abstract: | A series of experiments were carried out with direct metal laser sintering (DMLS) for the 316 stainless steel powders. During the laser sintering, due to the large liquid phase viscosity and surface tension, the balling effect occurred when the molten did not wet the solid metal particle and the underlying substrate. This resulted in a rough and bead-shaped surface, obstructing a smooth layer deposition. The balling effect of 316 stainless steel powder was studied, and the effects of process parameters, such as laser power, scan rate, and layer thickness, on the success of laser sintering were discussed. The results showed that increasing scan rate and decreasing laser power can minish balling effect to a certain extent. |
| |
| Keywords: | direct metal laser sintering metal powder balling effect process parameter |