钟罩型电子束焊接接头的疲劳寿命分析
引用本文:杨波,杨新华,付玮,胡树兵,肖建中.钟罩型电子束焊接接头的疲劳寿命分析[J].焊接学报,2011,32(5):69-72.
作者姓名:杨波  杨新华  付玮  胡树兵  肖建中
作者单位:1. 华中科技大学土木工程与力学学院,武汉,430074
2. 华中科技大学材料科学与工程学院,武汉,430074
摘    要:利用MSC公司的系列软件,模拟试验加载条件,将TC4钛合金钟罩型电子束焊接试件划分成焊缝、热影响区和母材3个区域,同时考虑热影响区材料强度的梯度分布,建立有限元模型,详细分析了焊件中的应力和疲劳寿命分布,沿不同观察路径考察了应力分布的规律,并将疲劳寿命分析结果与试验结果进行了比较.结果表明,焊缝对焊件的受力分布有明显影...

关 键 词:TC4钛合金  电子束焊接  钟罩型焊接接头  疲劳寿命
收稿时间:2010/3/1 0:00:00

Analysis of fatigue life of electron beam welding seam with bell shape
YANG Bo,YANG Xinhu,FU Wei,HU Shubing and XIAO Jianzhong.Analysis of fatigue life of electron beam welding seam with bell shape[J].Transactions of The China Welding Institution,2011,32(5):69-72.
Authors:YANG Bo  YANG Xinhu  FU Wei  HU Shubing and XIAO Jianzhong
Affiliation:School of Civil Engineering and Mechanics, Huazhong University of Science and Technology, Wuhan 430074, China,School of Civil Engineering and Mechanics, Huazhong University of Science and Technology, Wuhan 430074, China,School of Civil Engineering and Mechanics, Huazhong University of Science and Technology, Wuhan 430074, China,School of Materials Science and Engineering, Huazhong University of Science and Technology, Wuhan 430074, China and School of Materials Science and Engineering, Huazhong University of Science and Technology, Wuhan 430074, China
Abstract:The bell-shaped TC4 titanium alloy joint of electron beam welding were divided into three zones,namely weld seam,heat-affected zone and base metal.Considering the gradient distribution of the material strength in the heat-affected zone,the finite element model was founded.The series of software of MSC company were used to analyze the distribution of stress and fatigue life under the simulated experimental loading conditions,and the stress distribution along different paths were investigated,and the simulating results of fatigue life were compared with that of experiments.It is shown that the weld seam has noticeable effect on stress distribution of the weldment,which causes the stress concentration with the stress concentration factor of about 1.3 at the weld toe.The uneven distribution of weldment life is caused by stress concentration,so that the fatigue life of weldment is reduced.The fatigue failure usually starts at the weld toe.
Keywords:TC4 titanium alloy  electron beam welding  bell-shaped weld seam  fatigue life