锌/铝轧制复合研究
引用本文:李兴刚,齐克敏.锌/铝轧制复合研究[J].中国有色金属学报,1999,9(2):300-304.
作者姓名:李兴刚  齐克敏
作者单位:东北大学材料与冶金学院
摘    要:采用室温轧制复合法实验研究了锌/铝轧制复合时变形率和剥离强度的关系,通过界面电镜观测,探讨了锌/铝轧制的复合机理,同时提出了锌/铝复合板的热处理应选择低温、短时退火制度,以200℃,20min为宜。

关 键 词:轧制复合  临界变形率  剥离强度

COLD ROLLING OF ZnAl CLAD MATERIAL
Li Xinggang,Qi Kemin and Zhu Quan School of Materials and Metallurgy,Northeastern University,Shenyang ,P. R. China.COLD ROLLING OF ZnAl CLAD MATERIAL[J].The Chinese Journal of Nonferrous Metals,1999,9(2):300-304.
Authors:Li Xinggang  Qi Kemin and Zhu Quan School of Materials and Metallurgy  Northeastern University  Shenyang  P R China
Affiliation:Li Xinggang,Qi Kemin and Zhu Quan School of Materials and Metallurgy,Northeastern University,Shenyang 110006,P. R. China
Abstract:Characteristic bonding of Al/Zn sheets by cold rolling was studied. With the given data and SEM photographs, the following conclusions were obtained: During the process of rolling, virgin aluminum extrudes through cracks, and bonds are formed with oxidized and contaminated surfaces of Zn; to obtain good bonding strength, heat treatment of Zn/Al clad materials should be at a low temperature for a short time, especially at 200 for 20 min.
Keywords:clad rollingcritical deformationbonding strength