| 电流密度对Al/导电涂层/α-PbO2-CeO2-TiO2/β-PbO2-MnO2-WC-ZrO2复合电极材料制备和性能的影响 |
| |
| 引用本文： | 杨海涛,陈步明,郭忠诚,刘焕荣,张永春,黄惠,徐瑞东,付仁春.电流密度对Al/导电涂层/α-PbO2-CeO2-TiO2/β-PbO2-MnO2-WC-ZrO2复合电极材料制备和性能的影响[J].中国有色金属学会会刊,2014,24(10):3394-3404. |
| |
| 作者姓名： | 杨海涛 陈步明 郭忠诚 刘焕荣 张永春 黄惠 徐瑞东 付仁春 |
| |
| 作者单位： | 昆明理工大学 |
| |
| 基金项目： | Projects（51004056,51004057）supported by the National Natural Science Foundation of China;Project（KKZ6201152009）supported by the Opening Foundation of Key Laboratory of Inorganic Coating Materials,Chinese Academy of Sciences;Project（2010ZC052）supported by the Applied Basic Research Foundation of Yunnan Province,China;Project（20125314110011）supported by the Specialized Research Fund for the Doctoral Program of Higher Education,China;Project（2010247）supported by Analysis＆Testing Foundation of Kunming University of Science and Technology,China |
| |
| 摘 要： | 通过电化学氧化共沉积技术在A1/导电涂层/α-Pb O2-Ce O2-Ti O2基体上,制备了A1/导电涂层/α-PbO 2-Ce O2-Ti O2/β-Pb O2-MnO 2-WC-Zr O2复合阳极材料。通过能量色散X射线光谱（EDXS）、阳极极化曲线、暂稳态极化曲线（Tafel）、交流阻抗谱（EIS）、扫描电子显微镜（SEM）以及X射线衍射（XRD）等方法研究电流密度对复合阳极材料的化学组分、电化学活性和稳定性的影响。研究结果表明：在电流密度为1 A/dm2条件下制备的A1/导电涂层/α-PbO 2-Ce O2-Ti O2/β-PbO 2-MnO 2-WC-Zr O2复合材料具有最低的析氧过电位（0.610 V,条件：500 A/m2）,最好的电化学活性,最长的使用寿命（360 h,条件：150 g/L H2SO4,2 A/cm2,40°C）以及最低的槽电压（2.75 V,条件：500 A/m2）。而且,随着电流密度的增加,涂层晶粒逐渐增大,MnO 2含量也逐渐降低,晶体结构几乎没有变化。
|
| 关 键 词： | 复合电极材料 铝基体 β-PbO2-MnO2-WC-ZrO2 电化学共沉积 电流密度 |