Corrosion performance of high pressure die-cast Al-6Si-3Ni and Al-6Si-3Ni-2Cu alloys in aqueous NaCl solution

The corrosion performance of high pressure die-cast Al-6Si-3Ni (SN63) and Al-6Si-3Ni-2Cu (SNC632) alloys in 3.5% (mass fraction) NaCl solution was investigated. X-ray diffraction (XRD) and microstructural studies revealed the presence of single phase Si and binary Al₃Ni/Al₃Ni₂ phases along the grain boundary. Besides, the single Cu phase was also identified at the grain boundaries of the SNC632 alloy. Electrochemical corrosion results revealed that, the SNC632 alloy exhibited nobler shift in corrosion potential (?_corr), lower corrosion current density (J_corr) and higher corrosion resistance compared to the SN63 alloy. Equivalent circuit curve fitting analysis of electrochemical impedance spectroscopy (EIS) results revealed the existence of two interfaces between the electrolyte and substrate. The surface layer and charge transfer resistance (R_ct) of the SNC632 alloy was higher than that of the SN63 alloy. Immersion corrosion test results also confirmed the lower corrosion rate of the SNC632 alloy and substantiated the electrochemical corrosion results. Cu addition improved the corrosion resistance, which was mainly attributed to the absence of secondary Cu containing intermetallic phases in the SNC632 alloy and Cu presented as single phase.