花状CuO和花状CuO/石墨烯复合材料的制备及其在锂离子电池中的应用(英文)

采用水热法合成了花状CuO和花状CuO/石墨烯复合材料。采用XRD、SEM、TEM、BET、TG对材料的结构、形貌及性能进行表征和分析。花状CuO由CuO的纳米片组成,平均直径为4.2μm,比表面积为12.6m2/g。与花状CuO相比,花状CuO/石墨烯复合材料具有更高的充放电容量和更优良的循环稳定性。在0.1C、1C倍率下,其放电容量分别为603mA·h/g、382mA·h/g;在1C倍率下,经过50次循环,其容量保持率高达95.5%。

Preparation of uniform flower-like CuO and flower-like CuO/graphene composite and their application in lithium ion batteries

Flower-like CuO and flower-like CuO/graphene composite were prepared successfully by hydrothermal method. They were characterized by X-ray diffraction, scanning electron microscopy, nitrogen adsorption, temperature-programmed reduction, and thermogravimetric analysis. It is found that the flower-like CuO microspheres, which are composed of CuO nanosheets, possess an average diameter of 4.2 μm and a Brunauer–Emmett–Teller surface area of 12.6 m2/g. Compared with the flower-like CuO, the obtained flower-like CuO/graphene composite shows an enhanced electrochemical performance with a higher capacity of 603 mA-h/g at 0.1 C rate and 382 mA-h/g at 1 C rate, and exhibits a better cycle stability with a high capacity retention of 95.5 % after 50 cycles even though at 1 C rate.