| Preparation of highly dispersed antimony-doped tin oxide nanopowders by azeotropic drying with isoamyl acetate |
| |
| 作者姓名： | 杨芬 张学俊 吴旭 田芳 甘复兴 |
| |
| 作者单位： | [1]Department of Environmental Engineering, School of Resources and Environmental Science, Wuhan University, Wuhan 430079, China; [2]Department of Chemistry, Qujing Normal University, Qujing 655011,China; [3]Guizhou Province Key Laboratory of Ferment Engineering and Biological Pharmacy, Guizhou University, Guiyang 550003, China; [4]State Key Laboratory of Metal Corrosion and Protection, Institute of Metals Research, Chinese Academy of Sciences, Shenyang 110016, China |
| |
| 摘 要： | Antimony-doped tin hydroxide colloid precipitates were prepared by hydrolysis of SnCl4·5H2O and SbCl3 ethanol solutions. Isoamyl acetate was selected as azeotropic drying solvent and was compared with the most commonly used n-butanol solvent on treating precipitate for low hard agglomeration precursor powders. The FT-IR, BET, XRD, and TEM results of the precursor powders and calcinated antimony-doped tin oxide powders were recorded. The results demonstrate that isoamyl acetate is an excellent azeotropic drying solvent that can effectively prevent the agglomeration of particles and greatly improve the fluffiness of the obtained dried powders. After these precursor powders are calcined, antimony-doped tin oxide nanopowders with tetragonal futile structure and high dispersivity can be obtained.
|
| 关 键 词： | 锑元素 氧化锡 分散性 共沸干燥 异戊基 |
| 收稿时间： | 19 September 2006 |
| 修稿时间： | 2006-09-192007-03-19 |
Preparation of highly dispersed antimony-doped tin oxide nanopowders by azeotropic drying with isoamyl acetate |
| |
| YANG Fen,ZHANG Xue-jun,WU Xu,TIAN Fang,GAN Fu-xing.Preparation of highly dispersed antimony-doped tin oxide nanopowders by azeotropic drying with isoamyl acetate[J].Transactions of Nonferrous Metals Society of China,2007,17(3):626-632. |
| |
| Authors: | YANG Fen ZHANG Xue-jun WU Xu TIAN Fang GAN Fu-xing |
| |
| Affiliation: | 1.Department of Environmental Engineering, School of Resources and Environmental Science, Wuhan University, Wuhan 430079, China; 2. Department of Chemistry, Qujing Normal University, Qujing 65501 l,China; 3. Guizhou Province Key Laboratory of Ferment Engineering and Biological Pharmacy, Guizhou University, Guiyang 550003, China; 4. State Key Laboratory of Metal Corrosion and Protection, Institute of Metals Research, Chinese Academy of Sciences, Shenyang 110016, China |
| |
| Abstract: | Antimony-doped tin hydroxide colloid precipitates were prepared by hydrolysis of SnCl4-5H2O and SbCl3 ethanol solutions. Isoamyl acetate was selected as azeotropic drying solvent and was compared with the most commonly used n-butanol solvent on treating precipitate for low hard agglomeration precursor powders. The FT-IR, BET, XRD, and TEM results of the precursor powders and calcinated antimony-doped tin oxide powders were recorded. The results demonstrate that isoamyl acetate is an excellent azeotropic drying solvent that can effectively prevent the agglomeration of particles and greatly improve the fluffiness of the obtained dried powders. After these precursor powders are calcined, antimony-doped tin oxide nanopowders with tetragonal rutile structure and high dispersivity can be obtained. |
| |
| Keywords: | antimony-doped tin oxide nanopowder dispersivity azeotropic drying isoamyl acetate |