| 托板螺母冲压开裂原因分析 |
| |
| 引用本文： | 卢增威,翟丽丽.托板螺母冲压开裂原因分析[J].失效分析与预防,2011,6(1):36-39. |
| |
| 作者姓名： | 卢增威 翟丽丽 |
| |
| 作者单位： | 沈阳飞机工业集团有限公司,沈阳,110034 |
| |
| 摘 要： | 由0Cr17Ni5Mo3沉淀硬化不锈钢制造的托板螺母零件,在冲压拉伸成型过程中,在进行第一次及第二次冲压拉伸时零件发生开裂,大约有30%零件发生开裂.利用扫描电子显微镜、光学显微镜以及化学成分和力学性能的测试手段,对材料和断口进行深入研究,并开展了模拟试验.结果表明:裂纹是由于材料中的σ相引起的;最后确定了合适的固溶工...
|
| 关 键 词： | 螺母 开裂 重新固溶 |
Analysis of Deep-Drawing Cracking of Supporting-Plate Nuts |
| |
| LU Zeng-wei,ZHAI Li-li.Analysis of Deep-Drawing Cracking of Supporting-Plate Nuts[J].Failure Analysis and Prevention,2011,6(1):36-39. |
| |
| Authors: | LU Zeng-wei ZHAI Li-li |
| |
| Affiliation: | LU Zeng-wei, ZHAI Li,li (Shenyang Aircraft Group Industry Corporation Ltd., Shenyang 110034 ,China) |
| |
| Abstract: | Some supportingplate nuts of 0Cr17Ni5Mo3 PH stainless steel cracked during the process of deep drawing. In order to find out the failure cause, macro and micro observation, chemical composition analysis, and mechanical property testing were carried out. In addition, simulation tests were performed. The results show that cracks resulted from α phase in the material. This problem can be solved by adjusting the process of resolution. After proper resolution,α phase in the raw material for the nuts disappeared, and cracks did not occur during the following deep drawing process. |
| |
| Keywords: | nut cracking resolution |
| 本文献已被 CNKI 维普 万方数据 等数据库收录！ |
|