Mechanism of laser welding of SiC reinforced LD2 aluminum metal matrix composite |
| |
Authors: | Zhang Deku Chen Yanbin Niu Jitai Ji Guojuan |
| |
Affiliation: | National Key Laboratory of Advanced Welding Production Technology, Harbin Institute of Technology, Harbin, 150001;The State Key Laboratory of Metal Matrix Composites, Shanghai Jiaotong University, Shanghai, 200030 |
| |
Abstract: | In this paper the mechanism of SiC_P/LD2 aluminum matrix composites during laser welding was investigated. The emphasis was laid on the study of the distribution of aluminum carbides in whole welds. The joint can be divided into three regions both in depth and in width. The depth is divided into severe reaction region, partial reaction region, and no reaction region. In these regions, the extent of interfacial reaction varies gradually, the shape of reactants varies from long to fine. In width it can also be divided into severe reaction region, partial reaction region, and initial reaction region from the center of the weld to about the welding junction. In the initial reaction region, nucleation and growth of the reaction products on the surface of SiC particles can be observed by using TEM. The investigation showed that the quantity and size of SiC are relative to the temperature gradient in the molten pool. |
| |
Keywords: | SiC_P/LD2Al composites laser beam welding interfacial reaction temperature gradient |
本文献已被 CNKI 万方数据 等数据库收录! |
|