Strong bonding of infrared brazed α2-Ti3Al and Ti–6Al–4V using Ti–Cu–Ni fillers

Infrared dissimilar brazing of α₂-Ti₃Al and Ti–6Al–4V using Ti–15Cu–25Ni and Ti–15Cu–15Ni filler metals has been performed in this study. The brazed joint consists primarily of Ti-rich and Ti₂Ni phases, and there is no interfacial phase among the braze alloy, α₂-Ti₃Al and Ti–6Al–4V substrates. The existence of the Ti₂Ni intermetallic compound is detrimental to the bonding strength of the joint. The amount of Ti₂Ni decreases with increasing brazing temperature and/or time due to the depletion of Ni content from the braze alloy into the Ti–6Al–4V substrate during brazing. The shear strength of the brazed joint free of the blocky Ti₂Ni phase is comparable with that of the α₂-Ti₃Al substrate, and strong bonding can thus be obtained.